Image module

Polyethylene

UNIFOAM® XPE standard and special grades made from high quality polyethylene polymer and additives.

Select a product type from the list below:

PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³25±5
Tensile StrengthISO 1798kPa>130
Tensile ElongationISO 1798%>120
Compressive Strength
- deflection 10%ISO3386/1kPa>23
- deflection 25%>42
- deflection 50%>88
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤16
24 h after discharge%≤9
Thermal Conductivity
at 10 °CDIN52612W/mK0,034
at 40 °C0,037
Working Temperature RangeISO 2796°C-80/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->33
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³33±5
Tensile StrengthISO 1798kPa>176
Tensile ElongationISO 1798%>120
Compressive Strength
- deflection 10%ISO3386/1kPa>32
- deflection 25%>48
- deflection 50%>98
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤15
24 h after discharge%≤7
Thermal Conductivity
at 10 °CDIN52612W/mK0,036
at 40 °C0,039
Working Temperature RangeISO 2796°C-80/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->38
Horizontal Burn RateFMVSS-302mm/min<100
Flammability (20-60 mm thickness)DIN 4102-1-B2
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³33±5
Tensile StrengthISO 1798kPa>151
Tensile ElongationISO 1798%>85
Compressive Strength
- deflection 10%ISO3386/1kPa>29
- deflection 25%>45
- deflection 50%>88
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤17
24 h after discharge%≤8
Thermal Conductivity
at 10 °CDIN52612W/mK0,036
at 40 °C0,039
Working Temperature RangeISO 2796°C-40/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->38
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³45±6
Tensile StrengthISO 1798kPa>240
Tensile ElongationISO 1798%>120
Compressive Strength
- deflection 10%ISO3386/1kPa>60
- deflection 25%>76
- deflection 50%>142
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤12
24 h after discharge%≤5
Thermal Conductivity
at 10 °CDIN52612W/mK0,038
at 40 °C0,041
Working Temperature RangeISO 2796°C-80/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->46
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³45±6
Tensile StrengthISO 1798kPa>240
Tensile ElongationISO 1798%>105
Compressive Strength
- deflection 10%ISO3386/1kPa>60
- deflection 25%>76
- deflection 50%>142
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤14
24 h after discharge%≤7
Thermal Conductivity
at 10 °CDIN52612W/mK0,038
at 40 °C0,041
Working Temperature RangeISO 2796°C-40/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->46
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³60±8
Tensile StrengthISO 1798kPa>350
Tensile ElongationISO 1798%>170
Compressive Strength
- deflection 10%ISO3386/1kPa>110
- deflection 25%>120
- deflection 50%>190
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤12
24 h after discharge%≤5
Thermal Conductivity
at 10 °CDIN52612W/mK0,042
at 40 °C0,044
Working Temperature RangeISO 2796°C-40/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->58
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³100±10
Tensile StrengthISO 1798kPa>960
Tensile ElongationISO 1798%>100
Compressive Strength
- deflection 10%ISO3386/1kPa>160
- deflection 25%>180
- deflection 50%>270
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤9
24 h after discharge%≤5
Thermal Conductivity
at 10 °CDIN52612W/mK0,055
at 40 °C0,056
Working Temperature RangeISO 2796°C-40/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->28
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³120±15
Tensile StrengthISO 1798kPa>990
Tensile ElongationISO 1798%>110
Compressive Strength
- deflection 10%ISO3386/1kPa>200
- deflection 25%>230
- deflection 50%>320
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤8
24 h after discharge%≤4
Thermal Conductivity
at 10 °CDIN52612W/mK0,055
at 40 °C0,056
Working Temperature RangeISO 2796°C-40/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->33
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³140±15
Tensile StrengthISO 1798kPa>1100
Tensile ElongationISO 1798%>110
Compressive Strength
- deflection 10%ISO3386/1kPa>210
- deflection 25%>250
- deflection 50%>350
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤8
24 h after discharge%≤4
Thermal Conductivity
at 10 °CDIN52612W/mK0,060
at 40 °C0,061
Working Temperature RangeISO 2796°C-40/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->38
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³200±30
Tensile StrengthISO 1798kPa>1700
Tensile ElongationISO 1798%>110
Compressive Strength
- deflection 10%ISO3386/1kPa>400
- deflection 25%>450
- deflection 50%>650
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤6
24 h after discharge%≤4
Thermal Conductivity
at 10 °CDIN52612W/mK0,07
at 40 °C0,072
Working Temperature RangeISO 2796°C-40/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->43
Horizontal Burn RateFMVSS-302mm/min<100

Determination of bulk density DIN ISO 845

According to the norm the density is measured on the full thickness after removal of the skins. The test pieces are 100 mm x 100 mm x net thickness. Please note smaller pieces cutted out from the middle of the bun may have lower density.

Compressive Stress DIN ISO 3386-1

According to the norm the compressive strength is measured on a test specimen, which has a width/thickness ratio of 2:1 ( 50mm x 50mm x 25mm) and a surface of 25cm2. The speed is 100mm/min.
Differing from the norm the force is read in the first cycle.

Determination of compression set DIN EN ISO 1856

Differing from the norm the test piece is deflected by 25% of its thickness and held for 22 h at room temperature of 23º C.

Test for dimensional stability DIN EN ISO 2796

Differing from the norm the specimen is tested only by dry conditions in a temperature but not humidity controlled chamber.

This information is presented to our best knowledge. All test data are average values and should be considered as guidelines only.
Release date: 1 October 2018

Image module

Ethylene Vinyl Acetate

UNIFOAM® XVA made from high quality Ethylene Vinyl Acetate copolymer in densities ranging from 33 kg/m³ to 300 kg/m³

Select a product type from the list below:

PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³33±5
Tensile StrengthISO 1798kPa>190
Tensile ElongationISO 1798%>230
Compressive Strength
- deflection 10%ISO3386/1kPa>12
- deflection 25%>28
- deflection 50%>70
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤20
24 h after discharge%≤8
Thermal Conductivity
at 10 °CDIN52612W/mK0,035
at 40 °C0,039
Working Temperature RangeISO 2796°C-40/+55
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤3
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->23
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³45±6
Tensile StrengthISO 1798kPa>235
Tensile ElongationISO 1798%>230
Compressive Strength
- deflection 10%ISO3386/1kPa>17
- deflection 25%>35
- deflection 50%>80
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤15
24 h after discharge%≤5
Thermal Conductivity
at 10 °CDIN52612W/mK0,039
at 40 °C0,041
Working Temperature RangeISO 2796°C-40/+60
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤2,6
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->30
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³45±6
Tensile StrengthISO 1798kPa>215
Tensile ElongationISO 1798%>210
Compressive Strength
- deflection 10%ISO3386/1kPa>17
- deflection 25%>35
- deflection 50%>80
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤17
24 h after discharge%≤6
Thermal Conductivity
at 10 °CDIN52612W/mK0,039
at 40 °C0,041
Working Temperature RangeISO 2796°C-40/+60
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤2,6
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->30
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³60±8
Tensile StrengthISO 1798kPa>380
Tensile ElongationISO 1798%>300
Compressive Strength
- deflection 10%ISO3386/1kPa>40
- deflection 25%>55
- deflection 50%>110
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤10
24 h after discharge%≤4
Thermal Conductivity
at 10 °CDIN52612W/mK0,051
at 40 °C0,052
Working Temperature RangeISO 2796°C-40/+65
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00 internalISO 868->35
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³100±10
Tensile StrengthISO 1798kPa>990
Tensile ElongationISO 1798%>165
Compressive Strength
- deflection 10%ISO3386/1kPa>80
- deflection 25%>110
- deflection 50%>200
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤10
24 h after discharge%≤5
Thermal Conductivity
at 10 °CDIN52612W/mK0,051
at 40 °C0,052
Working Temperature RangeISO 2796°C-40/+65
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->18
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³120±15
Tensile StrengthISO 1798kPa>990
Tensile ElongationISO 1798%>180
Compressive Strength
- deflection 10%ISO3386/1kPa>90
- deflection 25%>120
- deflection 50%>200
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤7
24 h after discharge%≤4
Thermal Conductivity
at 10 °CDIN52612W/mK0,051
at 40 °C0,052
Working Temperature RangeISO 2796°C-40/+65
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->23
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³140±15
Tensile StrengthISO 1798kPa>1200
Tensile ElongationISO 1798%>200
Compressive Strength
- deflection 10%ISO3386/1kPa>140
- deflection 25%>180
- deflection 50%>300
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤7
24 h after discharge%≤4
Thermal Conductivity
at 10 °CDIN52612W/mK0,051
at 40 °C0,052
Working Temperature RangeISO 2796°C-40/+65
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->28
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³200±30
Tensile StrengthISO 1798kPa>1700
Tensile ElongationISO 1798%>200
Compressive Strength
- deflection 10%ISO3386/1kPa>200
- deflection 25%>280
- deflection 50%>400
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤7
24 h after discharge%≤3
Thermal Conductivity
at 10 °CDIN52612W/mK0,075
at 40 °C0,077
Working Temperature RangeISO 2796°C-40/+70
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->35
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³300±30
Tensile StrengthISO 1798kPa>2500
Tensile ElongationISO 1798%>200
Compressive Strength
- deflection 10%ISO3386/1kPa>400
- deflection 25%>550
- deflection 50%>650
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤6
24 h after discharge%≤3
Thermal Conductivity
at 10 °CDIN52612W/mK0,102
at 40 °C0,107
Working Temperature RangeISO 2796°C-40/+75
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->45
Horizontal Burn RateFMVSS-302mm/min<100

Determination of bulk density DIN ISO 845

According to the norm the density is measured on the full thickness after removal of the skins. The test pieces are 100 mm x 100 mm x net thickness. Please note smaller pieces cutted out from the middle of the bun may have lower density.

Compressive Stress DIN ISO 3386-1

According to the norm the compressive strength is measured on a test specimen, which has a width/thickness ratio of 2:1 ( 50mm x 50mm x 25mm) and a surface of 25cm2. The speed is 100mm/min.
Differing from the norm the force is read in the first cycle.

Determination of compression set DIN EN ISO 1856

Differing from the norm the test piece is deflected by 25% of its thickness and held for 22 h at room temperature of 23º C.

Test for dimensional stability DIN EN ISO 2796

Differing from the norm the specimen is tested only by dry conditions in a temperature but not humidity controlled chamber.

This information is presented to our best knowledge. All test data are average values and should be considered as guidelines only.
Release date: 1 October 2018

Special grades

UNIFOAM® XVA made from high quality Ethylene Vinyl Acetate copolymer in densities ranging from 33 kg/m³ to 300 kg/m³

Select a product type from the list below:

PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³33±5
Tensile StrengthISO 1798kPa>176
Tensile ElongationISO 1798%>120
Compressive Strength
- deflection 10%ISO3386/1kPa>32
- deflection 25%>48
- deflection 50%>98
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤15
24 h after discharge%≤7
Thermal Conductivity
at 10 °CDIN52612W/mK0,036
at 40 °C0,039
Working Temperature RangeISO 2796°C-40/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E12
Shore Hardness 00internal->38
Horizontal Burn RateFMVSS-302mm/min<100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³33±5
Tensile StrengthISO 1798kPa>176
Tensile ElongationISO 1798%>120
Compressive Strength
- deflection 10%ISO3386/1kPa>32
- deflection 25%>48
- deflection 50%>98
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤15
24 h after discharge%≤7
Thermal Conductivity
at 10 °CDIN52612W/mK0,036
at 40 °C0,039
Working Temperature RangeISO 2796°C-40/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->38
Horizontal Burn RateFMVSS-302mm/minSE
Flammability (20-60 mm thickness)DIN 4102-1-B2
Flammability (6-13 mm thickness)UL 94 HBF-HF-2
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³35±6
Tensile StrengthISO 1798kPa>176
Tensile ElongationISO 1798%>55
Compressive Strength
- deflection 10%ISO3386/1kPa>32
- deflection 25%>48
- deflection 50%>98
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤15
24 h after discharge%≤7
Thermal Conductivity
at 10 °CDIN52612W/mK0,036
at 40 °C0,039
Working Temperature RangeISO 2796°C-80/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00 internalinternal->38
Horizontal Burn RateFMVSS-302mm/minSE
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³170±15
Tensile StrengthISO 1798kPa>1500
Tensile ElongationISO 1798%>95
Compressive Strength
- deflection 10%ISO3386/1kPa>550
- deflection 25%>600
- deflection 50%>800
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤7
24 h after discharge%≤4
Thermal Conductivity
at 10 °CDIN52612W/mK0,060
at 40 °C0,061
Working Temperature RangeISO 2796°C-40/+90
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00 internalbelső->43
Horizontal Burn RateFMVSS-302mm/min100
PropertyTest
Standard
UnitNominal
value
DensityISO 845kg/m³60±6
Tensile StrengthISO 1798kPa>400
Tensile ElongationISO 1798%>270
Compressive Strength
- deflection 10%ISO3386/1kPa>16
- deflection 25%>30
- deflection 50%>85
Compression Set
22 h charge, 23 °C deflection 25%
0.5 h after dischargeISO1856%≤16
24 h after discharge%≤6
Thermal Conductivity
at 10 °CDIN52612W/mK0,042
at 40 °C0,044
Working Temperature RangeISO 2796°C-40/+65
Dimensional StabilityISO 2796%<5%
Water Absorption (7 days)DIN 53428vol.%≤1
Specific Volume ResistanceDIN 60093Ωcm≥10E15
Shore Hardness 00internal->20
Horizontal Burn RateFMVSS-302mm/min< 100

Determination of bulk density DIN ISO 845

According to the norm the density is measured on the full thickness after removal of the skins. The test pieces are 100 mm x 100 mm x net thickness. Please note smaller pieces cutted out from the middle of the bun may have lower density.

Compressive Stress DIN ISO 3386-1

According to the norm the compressive strength is measured on a test specimen, which has a width/thickness ratio of 2:1 ( 50mm x 50mm x 25mm) and a surface of 25cm2. The speed is 100mm/min.
Differing from the norm the force is read in the first cycle.

Determination of compression set DIN EN ISO 1856

Differing from the norm the test piece is deflected by 25% of its thickness and held for 22 h at room temperature of 23º C.

Test for dimensional stability DIN EN ISO 2796

Differing from the norm the specimen is tested only by dry conditions in a temperature but not humidity controlled chamber.

This information is presented to our best knowledge. All test data are average values and should be considered as guidelines only.
Release date: 1 October 2018

Pick colour

Our UNIFOAM®® XPE, XPE standard grades and XVA products are available in standard colours.

Any other colours required for whichever density are available on request.

  • Red 300
  • Blue 400
  • Yellow 200
  • Green 500
  • Pink 311
  • Beige 285
  • White 100
  • Silver Grey 150
  • Grey 700
  • Anthracite 800
  • Dark Black 950

Let’s start to work together!

We are always happy to answer your questions.

Contact Us
E-mails

sales@ufm.hu
sales2@ufm.hu

Address

9200 Mosonmagyaróvár,
Alkotmány utca 13.

Phone

+36 96 577 121
+36 96 577 122

GTC | Privacy statement Certificate